Quels sont les facteurs qui déterminent le taux de récupération de l'or par amalgamation ?

Amalgame d'or is a traditional method of extracting gold by binding it with mercury to form an amalgam, which is then heated to isolate pure gold. While historically significant, this process presents concerns due to mercury’s toxicity and environmental risks. The recovery rate—the efficiency of gold extraction via amalgamation—is influenced by multiple factors, including gold particle size, mercury quality, slurry concentration, pH levels, and temperature. Modern mining increasingly favors safer alternatives like cyanide leaching, but understanding amalgamation’s mechanics remains relevant for legacy operations and regulatory contexts.

Qu'est-ce que l'amalgamation de l'or ?

Amalgame d'or is a method of extracting gold from its ores by mixing it with mercury. It is an ancient gold separation method. This process forms a amalgame or-mercureLes particules d'or sont chimiquement liées au mercure. L'amalgame est ensuite chauffé pour vaporiser le mercure et laisser l'or. Cette technique a toujours été utilisée dans les mines d'or, en particulier dans les régions où l'or est finement disséminé dans le minerai et n'est pas facilement récupérable par d'autres méthodes.

Taux de récupération de l'amalgame d'or

Les taux de récupération de l'amalgame d'or se réfère au pourcentage d'or qui peut être récupéré avec succès par le processus d'amalgamation. Il mesure l'efficacité de la méthode d'extraction de l'or qui consiste à utiliser du mercure pour former un amalgame or-mercure.

Le taux de récupération est calculé en comparant la quantité d'or récupérée par amalgamation à la quantité totale d'or présente dans le minerai ou le concentré. Il est exprimé en pourcentage et donne une idée de l'efficacité du processus d'amalgamation pour capturer et extraire l'or de la matière première.

Un taux de récupération élevé indique qu'une plus grande proportion de l'or contenu dans le minerai est amalgamée et récupérée avec succès. Un taux de récupération plus faible indique qu'une quantité importante d'or n'est pas récupérée ou est perdue au cours du processus. Les pratiques minières modernes visent à maximiser les taux de récupération tout en minimisant les risques pour l'environnement et la santé liés à l'utilisation du mercure dans l'amalgamation de l'or.

Facteurs affectant le taux de récupération de l'or par amalgamation

Le taux de récupération de l'or lors de l'amalgamation au mercure dépend des facteurs suivants the particle size and shape of natural gold, the color of gold particles, the quality of mercury, the mercury amalgamation temperature, the slurry concentration, the mercury amalgamation method, and equipment factors, etc.

1. Gold Particle Size and Shape

The particle size, shape, and monomer dissociation degree of gold are mainly related to the grinding operation. In particular, the degree of monomer dissociation has a more significant impact. Increasing the grinding fineness can improve the recovery rate of mercury amalgamation operations. Gold particles suitable for mercury amalgamation generally are 0.2-0.3 mm. The lower limit of the mercury amalgamation plate particle size in the grinding cycle is 0.015 mm, but the fine gold particles are lost with the slurry.

2. La finesse des grains d'or

La couleur de l'or placérien est plus élevée que celle de l'or jaune. or filonien, and the color of gold in the oxidation zone is higher than that of primary ore. Gold with a high color is prone to amalgamation with mercury. If the surface of gold particles is contaminated, their amalgamation ability will significantly reduce.

3. Méthode d'amalgamation du mercure

L'amalgamation du mercure est divisée en l'amalgame interne de mercure et l'amalgame externe de mercure. External mercury amalgamation is mixing mercury to extract gold outside the crushing chamber. External mercury amalgamation is commonly used in China with fixed and vibrating mercury amalgamation plates. Internal mercury amalgamation is performed outside the crushing chamber. During the grinding operation cycle, mercury amalgamation is used to extract gold. Gold mines in South Africa and the United States often use mercury amalgamation in ramming machines. Small and medium-sized gold mines in the Soviet Union often use disc rollers. In China, mercury amalgamation cylinders are often used. The efficiency of internal mercury amalgamation is higher than that of external mercury amalgamation, and the quality of mercury gold is good. The concentration of external amalgamated mercury slurry should not be too high to form a loose, thin slurry flow, and the flow rate should not be too high to allow gold particles to settle onto the mercury plate. The concentration of internal mercury slurry should be 30-50%, and the mercury should be suspended.

4. pH du lisier

Le pH de la boue a une grande influence sur l'effet d'amalgamation du mercure. L'effet d'amalgame du mercure est bon en milieu acide et dans les solutions de cyanure, mais lorsqu'il y a beaucoup de boue, le milieu acide ne peut pas agglomérer la boue, et celle-ci contamine la surface des particules d'or, ce qui affecte l'effet d'amalgame du mercure. Lorsque le mercure est mélangé à un milieu alcalin, par exemple en utilisant de la chaux comme régulateur pour précipiter les sels solubles et éliminer les effets négatifs de la qualité de l'huile, l'impact du mélange de mercure est meilleur lorsque le PH est compris entre 8 et 8,5.

5. Masse de mercure

La qualité du mercure influence grandement l'effet de l'amalgamation au mercure. Le mercure pur ne permet pas de mouiller l'or. Le mercure contenant une petite quantité d'or, d'argent et de métaux communs peut réduire la tension superficielle du mercure et améliorer l'effet de mouillage. L'huile de moteur, d'autres matières organiques et la boue fine contaminent la surface des particules d'or. Le minerai sulfuré, le talc, le graphite et l'arséniure présents dans le minerai adhèrent facilement à la surface du mercure, ce qui affecte également la capacité de mouillage du mercure sur l'or.

When mixing mercury, add an appropriate amount of mercury. Too much will reduce the elasticity and consistency of the mercury paste, causing the amalgam to be lost with the slurry. Insufficient addition of mercury makes the mercury paste hard and loses its elasticity, reducing its gold-capturing performance. After the mercury board is put into production, the initial mercury coating amount is 15-30 grams/cubic meter, and mercury is added after 6-12 hours. The amount of mercury added is 2-5 times the gold content of the ore, and the consumption of mercury is usually 3-8 g/ton of ore.

6. Température d'amalgamation

In addition, temperature also affects the effect of mercury amalgamation. If the temperature is too low, it will increase the viscosity of mercury and affect the mercury amalgamation effect. If the temperature is too high, it will increase the fluidity of mercury, causing some of it to be lost. Therefore, the mercury amalgamation index is prone to seasonal changes. The mercury amalgamation temperature should generally be greater than 15 degrees. Adding mercury and adjusting the slurry concentration are used to eliminate the influence of temperature.

Conclusion: Balancing Efficiency and Sustainability

While amalgamation can achieve high recovery rates under optimal conditions, its reliance on toxic mercury demands caution. Modern alternatives such as cyanide leaching and gravity separation now dominate the industry, prioritizing environmental and worker safety. For operations still employing amalgamation, meticulous control of the above factors—particle size, gold purity, method selection, slurry chemistry, mercury quality, and temperature—is essential to maximize yields and minimize harm.